P. E . Separator
Value | Tol. | |
---|---|---|
Blackweb | 0.20 – 0.25 mm | +/- 0.03 |
Overall | 0.80 – 1.20 mm | +/- 0.05 |
Width | 120 – 124 mm | +/- 0.5 |
Shoulder width | 18 mm | +/- 4.0 |
Rib distance | 11 mm |
Value | Tol. | |
---|---|---|
Blackweb 0.25 mm | 80 mChm - cm² | +/- 0.03 |
Value | Tol. | ||
---|---|---|---|
Average pore size | 0.1 Micron | ||
Volume porosity | 60% | +/- 3 | |
Oil content | Total | 14% | +/- 3 |
B/W | 12% | +/-2 | |
Ash content | 65% | +/- 3 | |
Elongation | MD | 70% | min. |
CMD | 300% | min. | |
Tensile strength | MD | 6.5 N/m² | min. |
CMD | 3.5 N/m² | min. | |
Puncture strength | 8 N | min. | |
Moisture | 3% | max. | |
Wettability | 30 sec. | max. | |
Acid weight loss | 5% | max. | |
Shrinkage | 3% | max. | |
Trace elements | |||
Iron | 100 ppm | max. | |
Manganese | 5 ppm | max. | |
Chloride | 220 ppm | max. | |
Copper | 2 ppm | max. |
Value | Tol. | |
---|---|---|
Blackweb | 0.20 – 0.25 mm | +/- 0.03 |
Overall | 1.00 – 1.20 mm | +/- 0.05 |
Width | 120 – 126 mm | +/- 0.5 |
Shoulder width | 18 mm | +/- 4.0 |
Rib distance | 11 mm |
Value | Tol. | |
---|---|---|
Blackweb 0.25 mm | 80 m0Chm - cm² | max. |
Value | Tol. | ||
---|---|---|---|
Average pore size | 0.1 Micron | ||
Volume porosity | 60% | +/- 3 | |
Oil content | Total | 14% | +/- 3 |
B/W | 12% | +/-2 | |
Ash content | 65% | +/- 3 | |
Elongation | MD | 70% | min. |
CMD | 300% | min. | |
Tensile strength | MD | 6.5 N/m² | min. |
CMD | 3.5 N/m² | min. | |
Puncture strength | 8 N | min. | |
Moisture | 3% | max. | |
Wettability | 30 sec. | max. | |
Acid weight loss | 5% | max. | |
Shrinkage | 3% | max. | |
Trace elements | |||
Iron | 100 ppm | max. | |
Manganese | 5 ppm | max. | |
Chloride | 220 ppm | max. | |
Copper | 2 ppm | max. |
Value | Tol. | |
---|---|---|
Blackweb | 0.20 – 0.25 mm | +/- 0.03 |
Overall | 1.00 – 1.20 mm | +/- 0.05 |
Width | 150 – 155 mm | +/- 0.5 |
Shoulder width | 18 mm | +/- 4.0 |
Rib distance | 13.3 mm |
Value | Tol. | |
---|---|---|
Blackweb 0.25 mm | 80 mChm - cm² | max. |
Value | Tol. | ||
---|---|---|---|
Average pore size | 0.1 Micron | ||
Volume porosity | 60% | +/- 3 | |
Oil content | Total | 14% | +/- 3 |
B/W | 12% | +/-2 | |
Ash content | 65% | +/- 3 | |
Elongation | MD | 70% | min. |
CMD | 300% | min. | |
Tensile strength | MD | 6.5 N/m² | min. |
CMD | 3.5 N/m² | min. | |
Puncture strength | 8 N | min. | |
Moisture | 3% | max. | |
Wettability | 30 sec. | max. | |
Acid weight loss | 5% | max. | |
Shrinkage | 3% | max. | |
Trace elements | |||
Iron | 100 ppm | max. | |
Manganese | 5 ppm | max. | |
Chloride | 220 ppm | max. | |
Copper | 2 ppm | max. |
Value | Tol. | |
---|---|---|
Blackweb | 0.20 – 0.25 mm | +/- 0.03 |
Overall | 1.30 – 1.45 mm | +/- 0.05 |
Width | 158 – 162 mm | +/- 0.5 |
Shoulder width | 18 mm | +/- 4.0 |
Rib distance | 13.3 mm |
Value | Tol. | |
---|---|---|
Blackweb 0.25 mm | 80 mChm - cm² | max. |
Value | Tol. | ||
---|---|---|---|
Average pore size | 0.1 Micron | ||
Volume porosity | 60% | +/- 3 | |
Oil content | Total | 14% | +/- 3 |
B/W | 12% | +/-2 | |
Ash content | 65% | +/- 3 | |
Elongation | MD | 70% | min. |
CMD | 300% | min. | |
Tensile strength | MD | 6.5 N/m² | min. |
CMD | 3.5 N/m² | min. | |
Puncture strength | 8 N | min. | |
Moisture | 3% | max. | |
Wettability | 30 sec. | max. | |
Acid weight loss | 5% | max. | |
Shrinkage | 3% | max. | |
Trace elements | |||
Iron | 100 ppm | max. | |
Manganese | 5 ppm | max. | |
Chloride | 220 ppm | max. | |
Copper | 200 ppm | max. |